    Fremstilling og testing av PBXN-110

    View/Open
    09-01111.pdf (3.422Mb)
    Date
    2009
    Author
    Nevstad, Gunnar Ove
    Metadata
    Show full item record
    Abstract
    To partier av HMX krystaller med krystallfordeling tilsvarende klasse 2 og 3 har vært benyttet til fremstilling av PBXN-110 med 87.2 vektprosent HMX. Hensikten med fremstilling av PBXN110 var å studere om benyttede krystaller kunne ha forbedrede egenskaper med hensyn på sjokkfølsomhet. I Intermediate Scale Gap test ga undersøkt komposisjon en sjokkfølsomhet på 38.5 kbar, et resultat ikke ulikt hva vi normalt har oppnådde for PBXN-110. Derfor tyder resultatet på at benyttet krystall-sats 482/06 og sats 835/08 ikke har RS(Reduced Sensitivity) egenskaper av betydning selv om oppnådd sjokkfølsomhet ligger i det nedre området av hva som er rapportert i litteraturen for PBXN-110. Etter herding i 4 døgn ved 50 o C ble gjennomsnittlig Shore A15s hardhet målt til 34.6 et resultat som tilfredsstiller kravet på 20. Ved benyttet metode, hvor en kjegle av sprengstoffet initieres, er kritisk diameter funnet å være 3.8+0.2 mm. Detonasjonshastigheten er bestemt til 8233 m/s og detonasjonstrykket ved bruk av Plate Dent test til 242 kbar. De to siste resultatene er i overensstemmelse med Cheetah beregninger.
     
    Two charges of HMX crystals with crystal size distribution as class 2 and 3 have been used in production of PBXN-110 with 87.2 wt. % HMX. The purpose of the production of PBXN-110 was to study if used crystals could give improved properties with regard to shock sensitivity. In Intermediate Scale Gap test the study composition gave a shock sensitivity of 38.5 kbar, a result in accordance with what we normally have achieved for PBXN-110. The obtained shock sensitivity of PBXN-110 indicate the used crystals sats 482/06 and sats 835/09 have no RS (reduced Sensitivity) properties, even though the obtained shock sensitivity was in the lower range of what is reported in the literature for shock sensitivity of PBXN-110. Curing for 4 days at 50o C gave a composition that satisfies the requirement for Shore A15s hardness of 20 since our average result was 34.6. The average critical diameter determined by initiating a cone of the explosive was found to be 3.8+0.2 mm. Detonation velocity has been measured to 8233m/s, and the detonation pressure measured by use of Plate Dent test to 242 kbars. The last two results are in accordance with Cheetah calculated values.
     
    URI
    http://hdl.handle.net/20.500.12242/2300
    Collections
    • Rapporter

    Browse

    All of FFI PublicationsCommunities & CollectionsBy Issue DateAuthorsTitlesThis CollectionBy Issue DateAuthorsTitles

    My Account

    Login

    CONTACT US

    • FFI Kjeller
      FFI, PO Box 25, 2027 Kjeller
    • Office Address: Instituttvn 20,
      Phone 63 80 70 00
    • biblioteket@ffi.no

    HELPFUL

    • About FFI
    • Career
    • Reports

    Sitemap

    • About cookies (cookies)
    • Newsletter
    • Sitemap

    FOLLOW US

     

     

    © Copyright Norwegian Defence Research Establishment
    Powered by KnowledgeArc